RE: Anti-static (Pink-poly) film - affects on polycarbonate

Posted By Robert Vermillion 10-01-2021 06:59 AM
Found In Egroup: All Member Forum \ view thread
Hello Wesley, Andy Malcolm, thank you for your kind words. As a matter of fact, I do have an extensive background about antistatic transfer issues with antistatic PETG vacuum formed trays, antistatic pink poly, antistatic bubble, antistatic polyurethane & polyethylene foams, antistatic films, ...

RE: 100% Recycled Content in Corrugated Box Board

Posted By Robert Vermillion 11-21-2020 07:09 PM
Found In Egroup: All Member Forum \ view thread
Hello Sara, Asia Pacific linerboard may have been produced off a Cylinder Machine in the production of layered linerboard. Thus, the recycled content most likely would be much different than homogenous linerboard produced off a Fourdrinier machine. An Asia Pacific recycler may use bamboo, news clippings ...

RE: Thickness Measurement

Posted By Robert Vermillion 11-16-2020 04:35 AM
Found In Egroup: All Member Forum \ view thread
Hello Abhijeet, Ultrasonic thickness instruments are effective with various metals and polymers. A good digital micrometer Is from TESA Brown & Sharpe. Some companies will let you evaluate units for a week. Kind regards, Bob Vermillion All Member ForumPost New Message Nov 15, 2020Discussionsstarted ...

RE: Anti Static Additive cosmetic packaging

Posted By Robert Vermillion 08-04-2020 10:54 AM
Found In Egroup: All Member Forum \ view thread
Hello Shahzaad, Corrugated paperboard and polybags are charge generating in the right conditions. We have done extensive work in this area. There are advanced dust mitigating methods that could be incorporated. It is not uncommon to see ESA (electrostatic attraction) in bottling operations and the ...

RE: Comparison/Conversion of US ECT

Posted By Robert Vermillion 08-02-2020 09:18 AM
Found In Egroup: All Member Forum \ view thread
Hello Ken, Know your group well in the past at HP. I appreciate your comparison as was invloved with high performance liners years ago. Nice to keep up with your references. ------------------------------ Robert Vermillion CPPLT, Fellow Certified ESD & Product Safety Engineer-iNARTE RMV ...

RE: Anti Static Additive cosmetic packaging

Posted By Robert Vermillion 08-02-2020 09:10 AM
Found In Library: All Member Forum

RE: Anti Static Additive cosmetic packaging

Posted By Robert Vermillion 08-02-2020 09:10 AM
Found In Egroup: All Member Forum \ view thread
Hello Shahzaad, This is something that we could assit in evaluating your products. I would need to see if this would not be an ITAR issue. I would not be discouraged by what your suppliers state as their subject matter expertise may be limited, at best, on electrostatic attraction (ESA). ...

RE: Child Resistant Packaging

Posted By Robert Vermillion 06-26-2020 10:56 AM
Found In Egroup: All Member Forum \ view thread
Hello Vishnu, The American Counci of Independant Laboratories (ACIL) can put out an announcement to the members regarding your request. Contact Beth Horan: https://www.acil.org/page/713 Beth Horan Chief Financial Officer & Operations Manager (636) 265-2200 bhoran@acil.org Kind ...

RE: CPP Multiple Choice Exam

Posted By Robert Vermillion 05-22-2020 08:47 AM
Found In Egroup: All Member Forum \ view thread
Hello Savannah, Packaging engineering is very important to Space & Defense. Go with your 1st answer that comes to mind. Be well rested to be well tested. Best of luck and I am sure that you will do great! Kind regards, Bob Vermillion Bob Vermillion, CPP, Fellow Certified, ESD ...

RE: Corrugate Hot Melt Adhesive

Posted By Robert Vermillion 03-23-2019 10:28 AM
Found In Egroup: All Member Forum \ view thread
Sometimes, if one a replacement method cannot be found, organizations will use a testing method that has been abandoned if it still has merit or develop a testing method unique to your industry sector. Also, it would be good to review the Military documents that are free on-line since there could be ...

RE: Laboratory test conditions

Posted By Robert Vermillion 02-27-2019 11:19 AM
Found In Egroup: All Member Forum \ view thread
Hello James, In the ESD packaging & materials arena, 12%+/-3%RH is utilized for materials qualification. There are test methods that require both 12%+/-3%RH and 50%+/-3%RH at 73 Deg F+/- 5 Deg F. The preconditioning time can vary but 48 hours is minimum for most ESD tests. Some of the evaluations ...

RE: Barrier property aluminium vs metallized

Posted By Robert Vermillion 01-12-2019 09:13 AM
Found In Egroup: All Member Forum \ view thread
On another note: In my ESD evaluation of shielding barriers for electrostatic discharge attenuation from EMI/RFI Emissions, Aluminium Moisture Barrier Bags (Type 1) provide superior shielding (a true Faraday Cage at <1.0 nJ) over a vacuum deposited aluminium or zinc (Metallized Shielding bags, Type ...